Preferred orientation of carbon nanotubes in polyethylene

The extraordinary mechanical properties of carbon nanotubes can be used to improve the strength and other mechanical properties of polymer materials by hybriding carbon nanotubes into polymer materials. These nanotubes may have preferred orientation due to their natural shape. In the Figure 1 below, X-ray diffraction patterns from polyethylene with and without added double-wall carbon nanotubes measured in reflection geometry taken using Rigaku's SmartLab multipurpose diffractometer are presented. A carbon nanotube peak is clearly observed in the sample containing carbon nanotubes. However, this geometry does not reflect the orientation of the nanotubes in this material.


X-ray diffraction patterns from polyethylene


Figure 1

To determine the preferred orientation of the nanotubes, transmission X-ray diffraction measurements of the sample with carbon nanotubes were taken at different azimuths. The carbon nanotube peak was seen only in an orientation along which high order polyethylene peaks are presented, as in Figure 2 below. This suggests that the nanotubes are preferentially aligned along the same direction as the polyethylene chains.


Nanotube peak seen only in an orientation along which high order polyethylene peaks

Figure 2


The SmartLab is the most novel high-resolution diffractometer available today. Perhaps its most novel feature is the SmartLab Guidance software, which provides the user with an intelligent interface that guides you through the intricacies of each experiment. It is like having an expert standing by your side. Read more about SmartLab...

Ask for more info